UF Powdered Resins

Urea Formaldehyde Powder Resin AL 901P


Urea Formaldehyde Resin is a kind of polymer that belongs to a group known as Thermosetting Resin. Polymers belong to this group do not soften while being heated, and in fact become hardener due to the formation of additional cross-link between the molecules of the polymer.Due to its exceptional bond strength, water resistance and economical nature,Urea Formaldehyde Powdered Resin can be used for all sorts of wood based.

Application

  • Standard emission at the range of E2/E3
  • Glue for Plywood, Particle board, Medium Density Fibreboard, Chipboard Panels,Veneers, Doors,
  • Glue for furniture joints
  • Paint Coating

Specifications

PropertiesSpecifications
AppearanceFree flowing powder
SolubilitySoluble in water
Volatile Content (105˚C / 1 hr.)Max 3%
Free Formaldehyde (67% Solution)Max 2%
Viscosity at 30˚C (2:1 / 67% Solution)Min 1400 cps
pH at 30˚C (2:1 / 67% solution)7 - 9
Gel Time at boiling water (Reactivity)40 - 70 seconds
(50g of 67% sol. Mix + 2ml 25% hardener)
Gel T ime / Pot life at 30˚CMax 60 minutes
(50g of 67% sol. Mix + 2ml 25% hardener)

Storage

Store in the original bags in a cool place protected from heat. Keep away from absorb moisture.The bags should be carefully closed before storage.Storage life at 30°C : 12 months

Packing

Available in 25 kg/bag with woven bag and inner polyethylene liner.

Urea Formaldehyde Powder Resin AL 903P


Urea Formaldehyde Powder (AL903P) is a kind of polymer that belongs to a group known as Thermosetting Resin.

The AL903P easily mixed with water and used as liquid glue. It is formulated for the low emission level.

Application

  • low emission
  • Glue for Medium Density Fibreboard, Particle Board, Plywood and other cellulosic products

Specifications

PropertiesSpecifications
AppearanceWhite free flowing powder
SolubilitySoluble in water
Volatile Content (105˚C / 1 hr.)Max 3%
Free Formaldehyde (67% Solution)Max 2%
Viscosity at 30˚C (2:1 / 67% Solution)Min 1500 cps
pH at 30˚C (2:1 / 67% solution)8 - 10
Gel Time at boiling water (Reactivity)60 - 100 seconds
(50g of 67% sol. Mix + 2ml 25% hardener)

Storage

Store in the original bags in a cool place protected from heat. Keep away from absorb moisture and water.The bags, which have been opened, should be carefully closed before storage. Storage life at 30°C : 12 months

Packing

Available in 25 kg/bag with woven bag and inner polyethylene liner.

Melamine Urea Formaldehyde Powder Resin AL 905P


Melamine urea formaldehyde resins (AL 905P) are poly-condensation products of the reaction of formaldehyde with urea and melamine. AL 905P resins have higher water and weather resistance and therefore are suitable for the production of panels for exterior use or in conditions of high humidity. AL 905P resins provide panels with superior properties and this compensates their relatively higher raw material cost.

MUF 905P is melamine urea formaldehyde resin with 20% melamine content

Application

  • low emission
  • Particle Board, Medium Density Fibreboard (MDF), laminated veneer lumber (LVL) and Plywood.

Specifications

PropertiesSpecifications
AppearanceWhite free flowing powder
Viscosity at 30˚C (67% Solution)Min 600 cps
pH at 30˚C (67% solution)8 - 10
Volatile Content (105˚C / 1 hr.)Max 3%
Free Formaldehyde (67% Solution)Max 2%

Storage

Store in the original bags in a cool place protected from heat. Keep away from absorb moisture. The bags should be carefully closed before storage. Storage life at 30°C : more than 6 months

Packing

AL 905P vailable in 25 kg/bag with woven bag and inner polyethylene liner.

Melamine Urea Formaldehyde Powder Resin AL 907P


AL 907P, Melamine Urea formaldehyde resins are poly-condensation products of the reaction of formaldehyde with urea and melamine. AL 907P have higher water and weather resistance and therefore are suitable for the production of panels for exterior use or in conditions of high humidity. AL 907P resins provide panels with superior properties and this compensates their relatively higher raw material cost.

AL 907P is melamine urea formaldehyde resin with 10% melamine content

Application

  • Particle Board, Medium Density Fibreboard (MDF), laminated veneer lumber (LVL) and Plywood.
  • AL 907P for applications where boards with low formaldehyde emissions.

Specifications

PropertiesSpecifications
AppearanceWhite free flowing powder
Viscosity at 30˚C (67% Solution)Min 1000 cps
pH at 30˚C (67% solution)8 - 10
Volatile Content (105˚C / 1 hr.)Max 3%
Free Formaldehyde (67% Solution)Max 2%

Storage

Store in the original bags in a cool place protected from the heat. Keep away from absorb moisture and water. The bags, which have been opened, should be carefully closed before storage. Storage life at 20°C: more than 6 months

Packing

AL 907P is available in 25 kg/bag with woven bag and inner polyethylene liner.

Melamine Formaldehyde Powder Resin AL 102P


Melamine formaldehyde powder resin (AL 102P) is a powder form that can be used in the modification of urea glues by physical blending for achieving overall improved properties of wood boards, especially for enhanced moisture resistance. This is more common in case of plywood gluing. It is soluble in water and clear to slightly hazy solution.

Application

  • Glue for Particle Board, Medium Density Fibreboard (MDF), Plywood
  • Low emission
  • Impregnation of base / decorative paper

Specifications

PropertiesSpecifications
AppearanceWhite free flowing powder
SolubilitySoluble in water
Volat ile Content (105˚C / 1 hr.)Max 3%
Free Formaldehyde (50% Solution)Max 0.7%
Viscosity at 30˚C (2:1 / 50% Solution)Min 20 - 40 cps
pH at 30˚C (50% solution)8 - 10
Gel Time at boiling water (Reactivity)Max 100 seconds
(50g of 50% sol. Mix + 2ml 25% hardener)

Storage

Store in the original bags in a cool place protected from the heat. Keep away from absorb moisture and water. The bags, which have been opened, should be carefully closed before storage. Storage life at 20°C: more than 6 months

Packing

AL 102 P is available in 25 Kg/bag with woven bag and inner polyethylene Liner.

Melamine Formaldehyde Powder Resin AL 103P


Melamine formaldehyde powder resin (AL 103P) is a special type powder used for glazing of amino moulded articles. When used as a glazing compound it imparts very high gloss to the surface of the moulded article. The finished products exhibit excellent gloss, surface hardness, stain resistance, heat resistance and chemical resistance. It needs to be reconstituted into solution by dissolving in water for impregnation of paper.

Application

Decorative and overlay papers filled with melamine resin are used for :-

  • Lamination on particle boards.
  • Flooring market.
  • Decorative laminated boards, used in applications with heavy demands on e.g. Kitchen, lab, hospitals, etc.

Specifications

PropertiesSpecifications
AppearanceFree flowing powder
Volatile Content (105˚C / 1 hr.)Max 3%
Storage life 30˚CNot less than six months
Viscosity at 30˚C (50% Solution)20 - 40 cps
pH at 30˚C (50% solution)8 - 10

Storage

Store in the original bags in a cool place protected from the heat. Keep away from absorb moisture. The bags should be carefully closed before storage. Storage life at 20°C: more than 6 months

Packing

AL 103P is available in 25 Kg/bag with woven bag and inner polyethylene Liner.

Urea Formaldehyde one shot Powder Resin AL 1000P


AL 1000P adhesive is a filled, pre-catalyzed urea formaldehyde resin powder form.It only needs to be reconstituted with water prior to use. It does not require a hardener.

Application

Decorative and overlay papers filled with melamine resin are used for :-

  • Glue for laminating, doweling, veneering and other similar wood bonding operations where the resin is required to cure at room temperature
  • Glue for wooden furniture
  • Glue for wood flooring

Specifications

PropertiesSpecifications
AppearanceWhite Free flowing powder
SolubilitySoluble in water
Volatile Content (105˚C / 1 hr.)Max 3%
Free Formaldehyde (67% Solution)Max 2%
Viscosity at 30˚C (2:1 / 67% Solution)3000 - 5000 cps
pH at 30˚C (2:1 / 67% solution)4 - 6
Gel Time / Pot Life at 30˚C60 ± 15 minutes
Storage Life at room temperatureApprox. 6 months

Storage

Store the AL 1000P in a cool place protected from the heat. Heat and moisture will cause powder to harden thus rendering it useless.

Glue mix viscosity and gel time are expected to increase and decrease respectively when AL 1000P approaches end of storage life. Under such circumstances, the amount of water added to the glue mix should be increased to a maximum of 65 parts by weight. (Note: recommended glue mix). Storage life at 20 - 30°C: 6 months

Packing

AL 1000P is available in 25kg/bag with woven bag and inner polyethylene liner

TOP